Tunneling Spectroscopy Study of Low Baked Bulk Niobium for Superconducting RF Cavity Applications
In the authors' words
Point-contact tunneling (PCT) spectroscopy was used to probe the local superconducting properties of cavity-grade niobium following surface treatments representative of superconducting radio-frequency (SRF) cavities. Electropolished (EP) samples were compared with samples baked at 120~C for 48 h and subjected to a two-step bake at 75~C for 2 h followed by 120~C for 48 h. Although the superconducting gap is predominantly distributed around the bulk Nb value (~1.5 meV), regions exhibiting strongly suppressed gaps (minigaps) are observed in 15--29% of junctions on EP samples. Their occurrence decreases to 6% after the 120~C bake and to only 1% after the two-step treatment. Spectra exhibiting minigaps are well described by the Usadel proximity-effect model, consistent with superconducting Nb coupled to normal regions that we attribute to hydride formation. These results provide direct microscopic evidence that low-temperature baking suppresses regions of degraded surface superconductivity in cavity-grade Nb. The pronounced reduction achieved by the two-step bake further supports a link between hydride-related proximity effects and the surface superconducting properties governing SRF cavity performance.
Appeared: Monday, September 21. arXiv. Preprint, not yet peer-reviewed.